Technical Support

12 6月

Preparation and application of molybdenum silicate

Molybdenum Disilicide, MoSi2 is a kind of silicon Molybdenum compound, also known as Molybdenum Disilicide, Molybdenum silicide has high melting point, low density, good thermal conductivity and good electrical conductivity and excellent high temperature oxidation resistance, high elastic modulus, low thermal expansion coefficient, high strength, good resistance to chemical corrosion and thermal shock resistance, are widely used in high temperature heating element component materials and high temperature oxidation resistance coating materials, is also the most development potential of high [...]

Technical Support 详情...
23 5月

Main applications of tantalum silicide

Metal silicides are similar to metals in electrical conductivity, high temperature performance, oxidation resistance and compatibility with the production process of silicon integrated circuits. Transition metal silicides can be used for low-resistance gate and interwire, schottky gate and resistance contact. Tantalum silicide preparation method includes: the combustion synthesis (combustionsynthesis, CS) or self-propagating high-temperature synthesis, arc melting method, etc. Combustion synthesis or self-propagating high temperature synthesis is a method for the synthesis of intermetallic compounds by the exothermic reaction of [...]

Technical Support 详情...
15 5月

Preparation of zirconium tungstate

1.. Impregnation method A certain amount of zrocl2.8h20 was dissolved in an appropriate amount of deionized water, and ammonia was added to form a hydrogel. The pH value was adjusted to 9.0. After being placed at room temperature for 12h, the precipitate was filtered and washed with deionized water to be chlorine-free (0.1 mol·L ~ AgN03 solution was used for detection). Then the filter cake was soaked in anhydrous ethanol and alcoholized for 12 h in a constant temperature drying [...]

Technical Support 详情...
15 4月

Safety technical specification for ammonium metavanadate

Part one: chemical name Chinese name of chemical: ammonium metavanadate Chemical name: ammonium vanadate English name: chemicals ammonium metavanadate English name: ammonium vanadate Part 2: composition/composition information Harmful composition: ammonium metavanadate Content: ≥ 99% CAS No. 55-7803-6 Part iii: risk overview Risk category: Invasion route: Health hazards: dust can irritate the eyes, skin and respiratory tract. Death can be caused by inhalation and oral administration. Inhalation causes coughing, chest pain, pain, metallic taste in the mouth and mental symptoms. Have damage to liver, kidney. Skin contact can cause hives. Environmental hazards: harmful [...]

Technical Support 详情...
01 4月

Application of niobium silicide in material

Niobium (Nb) is a kind of refractory metal with high melting point (2468℃), moderate density, corrosion resistance, radiation resistance, and high temperature strength, with good mechanical properties at high temperature. The excellent properties of niobium and niobium alloy make it one of the important candidate materials for high-temperature structural parts in aviation, aerospace and nuclear industry, which can be used to manufacture rocket engines, nuclear reactors and other key components. However, its poor oxidation performance, pure niobium at 600℃ [...]

Technical Support 详情...
25 3月

The invention relates to a titanium aluminum carbon and titanium carbide composite hydrogen storage material and a preparation method thereof

Technical scheme of the invention are as follows: a carbon titanium aluminum and titanium carbide composite hydrogen storage material, its characteristic is: described in the composite hydrogen storage material is composed of the following components: titanium aluminum carbon for ternary compound, described the specific of Ti3AlC2 or Ti2AlC, titanium carbide described as TiCx, of which 0.48 x 0.8 or less, or less composite hydrogen storage materials of titanium aluminum carbon mass ratio of 2% to 15%, the rest for [...]

Technical Support 详情...
19 3月

A method for preparing molybdenum boride powder

A method of preparation of boride molybdenum powder preparation steps in the synthesis of high temperature and high pressure way, according to the synthetic before B/Mo mole ratio of n (n = 0.5, 1, 2, 2.5, 4) Settings, in full compliance with material control design phase of boride molybdenum powder, achieve the boride phase of molybdenum materials synthesis and controllable, and synthesis of boride molybdenum powder granularity and the crystal grain size is complete, excellent performance. The method has [...]

Technical Support 详情...
11 3月

A method for preparing large area monolayer tungsten selenide single crystal

The present invention relates to the field of microelectronics technology, in particular to a Chemical vapor deposition (CVD) method for the preparation of a single crystal of monolayer tungsten diselenide (WSe2). Background technology: With molybdenum disulfide (MoS2), two dock selenide (WSe2) represented by a two-dimensional function of transition metal chalcogenide materials in the process of multi-layer to single layer, can be achieved by indirect band gap to direct band gap, with its unique physical and chemical properties make it in electronic [...]

Technical Support 详情...
05 3月

Application of tungsten oxide

Tungsten oxide, also known as tungsten hua, chemical formula WO3. Pale yellow rhombic crystal, the color deepened when heated, and then returned to light yellow after cooling. Stable in air, melting point is 1473℃, boiling point is higher than 1750℃, relative density is 7. 16. Insoluble in water and inorganic acids except hydrofluoric acid, soluble in hot concentrated sodium hydroxide solution and ammonia water. Tungsten oxide is both an n-type semiconductor material and a “d0” oxide, which gives it [...]

Technical Support 详情...
15 1月

Preparation method of nanometer ferroferric oxide Fe3O4 particles

The development of nanotechnology has opened up a new field for the research of various materials. Nowadays, a variety of nanomaterials have been fully applied in the field of autocorrelation, and the value of nanomaterials has been fully affirmed. Therefore, the development of new nanomaterials has become a necessity of modern society, with great development prospects. Nanometer Fe3O4 has the characteristics of small particle size, high specific surface area and magnetic sensitivity. It has been widely applied in the [...]

Technical Support 详情...